Mactac 9700PRO High-Performance Translucent Vinyl Ultramarine Blue

Description

Mactac 9700PRO High-Performance Translucent Vinyl Ultramarine Blue
MACal 9700Pro
Translucent Vinyl Series
Product Description
MACal 9700Pro is a translucent high performance, 5-7 year outdoor film. The face is a matte finished 3-
mil cadmium-free vinyl. This product is available in a wide variety of bright, consistent, uniform
translucent colors. The film is coated with a durable permanent acrylic adhesive with excellent wet out
characteristics for clarity. An 83# white kraft liner offers stability and layflat. The product has good
dimensional stability and is designed for excellent cutting and weed ability. This product is specifically
designed for backlit applications.
Physical Properties
Property Typical Values Test Method
Thickness in inches
Film plus adhesive 0.0045 (115)
ASTM D-645
Peel Adhesion
180° on Stainless Steel
– 20 min.
– 24 hr.
– 1 week
4.6 (20)
5.0 (22)
5.5 (24)
ASTM D-903
Face Material Data
68°F (20°C)
Tensile strength lb. /in.
(N/15mm)
Elongation % at break
>9.8 (28)
>18%
DIN 53455
Dimensional Stability
(shrinkage) in Percent <0.02 (0.508)
FTM- 14
48 hours @ 158°F (70°C)
10” x 10” Sample
Bonded to aluminum
Temperature Ranges
Application:
End Use:
50° to 104°F (10° to 40°C)
-40° to 194°F (-40° to 90°C)
Flammability Self-extinguishing ISO 3795
Durability
The durability of these films is indoor and 5-7 years outdoors. This use-life estimate is based upon
accelerated age studies. Please note that exposure to severe temperatures, ultra-violet light and also
tropical, sub-tropical or desert regions will cause more rapid deterioration. This also applies to polluted
areas, high altitude and south facing exposure.
Shelf Life
Two years when stored at 75°F (24°C) and 50% relative humidity or less.
Chemical Resistance
A sample is prepared by adhering the film to a metal substrate 24 hours prior to immersion in the chemical
solution or solvent. After a fixed period of time, the sample is removed, dried and examined for adhesion.
Chemical Time Immersed Observation
Water 24 hours Excellent
5% Detergent 24 hours Excellent
10% Hydrochloric Acid 24 hours Excellent
10% Sulfuric Acid 24 hours Excellent
10% Phosphoric acid 24 hours Good
10% Sodium Hydroxide 24 hours Excellent
10% Ammonium Hydroxide 24 hours Excellent
Methanol 1 hour Good
Glass Breakage
MACtac accepts no liability for glass breakage due to temperature differences across the glass which can
be caused by sunlight on dark areas of the graphic. Size, thickness, quality of cut, edge treatment, tinting
and frame design all effect temperature stress.
Application
Care should be taken when selecting a substrate for use in illuminated devices with pressure-sensitive
materials. Some substrates, e.g. polycarbonate, can cause problems because of ‘bubbling’. It is
recommended that trials be conducted to establish the compatibility of MACal 9700Pro with the
application surface. Application of MACal 9700 is made easier if MACtac application tape is used.
Thermal Forming
Thermal form using a temperature between 280°- 320°F (140° and 160°C). This temperature (and
exposing time) differs according to:
• The thickness of the acrylic sheet
• The distance between the heat source & the panel
• The chemical nature of the panel (PMMA – PETG, etc.)
Note: it is important to apply 9700 on dry method and to wait few hours to get a right bond before
forming.
Limitations
1) The user is responsible for determining the product’s suitability, including adhesion and if
needed, removal characteristics when used in applications other than listed specifically in this
Performance Guide.
2) If there are any questions about applications, please contact your Mactac sales representative
to discuss your requirements for recommendations.
3) If this is a printed Performance Guide it is an uncontrolled document. Please check the Mactac
website for the latest, most up-to-date version.

9738-03 Ultramarine Blue