Orafol ORAGUARD 289F PVC-Free Laminating Film

Description

Orafol ORAGUARD 289F PVC-Free Laminating Film
ORAGUARD® 289F PVC-Free Laminating Film
Description
2-mil, premium PVC-free and plasticizer-free high performance laminating film, transparent with glossy surface and highest
level of UV protection.
Release Liner
1.4-mil polyester film, silicone-coated on one side
Adhesive
Clear, solvent-based, permanent
Area of Use
For protection of digitally printed large format images in indoor and outdoor graphic applications. Recommended for use with
PVC-free and plasticizer-free digital printing film ORAJET®
3981RA PVC-Free Wrapping Film with RapidAir®
technology.
Technical Data
Thickness (without liner and adhesive) 2-mil
Dimensional Stability (FINT TM 14) Adhered to steel, shrinkage 0.003 max.
Temperature Resistance Adhered to aluminum, -58°F to +212°F, no variation
Adhesive Power (FINAT TM-1, after 24 h, average) Adhered to stainless steel: 2.74 lb/in
Tensile Strength (DIN EN ISO 527) Along: Min. 25 MPa
Across: Min. 25 MPa
Elongation at Break (DIN EN ISO 527) Along: Min. 150%
Across: Min. 150%
Seawaterability (DIN 50 021) Adhered to aluminum, after 100h/73°F, no variation
Resistance to Solvents and Chemicals At room temperature, 72h after adhesion to aluminum,
short-term resistant to most oils and greases, fuels, aliphatic
solvents, weak acids, salts and alkalis
Shelf Life (68°F/50% relative humidity) 2 years
Minimum Life Expectancy
(based on accepted application procedures on vertical
surfaces, normal climate of Central Europe)
10 years
Minimum Application Temperature > +46°F
Available Lengths
Available Widths
150’ (50-yard), 30’ (10-yard)
54”, 60”
Recommended to be used in combination with ORAJET®
Series 3981RA
UV Protection Extension Factor + 4 Years
For best results, utilize ORAFOL ICC profiles available at www.orafolamericas.com and allow solvent-based inks to dry for at least 24 hours
(48-72 hours preferred) at 70°F before cutting the graphic to the ink or applying a laminate.