Orafol ORAGUARD 297GF Optically Clear Premium Cast PVC Laminating Film

Description

Orafol ORAGUARD 297GF Optically Clear Premium Cast PVC Laminating Film
ORAGUARD® 297F OPTICALLY CLEAR PREMIUM CAST PVC LAMINATING FILM
Description
2.75-mil, premium optically clear cast PVC film with a UV extension factor of four years. Available in gloss finish.
Release Liner
1.6-mil silicone-coated polyester film
Adhesive
Clear, solvent-based, permanent adhesive
Applications
Especially developed for protection of the printed ORAJET® Window-Graphics films. The laminating film with its
optimized hardness covers the perforated film so that no humidity, dust or other contaminations can penetrate
the perforation of the film.
Technical Data
Thickness (without liner and adhesive) 2.75-mil
Temperature Resistance Adhered to aluminum, -58°F to +230°F, no variation
Fire Behavior (DIN 75200)
Fire Rating
Adhered to steel, self-extinguishing
ASTM E 84-07 Class “A”
Adhesive Power (FINAT TM-1, after 24 h, average) Adhered to stainless steel: 2.74 lb/in
Tensile Strength (DIN EN ISO 527) Along: Min. 19 MPa
Across: Min. 19 MPa
Elongation at Break (DIN EN ISO 527) Along: Min. 120%
Across: Min. 120%
Seawaterability (DIN 50 021) Adhered to aluminum, after 100h/73°F, no variation
Shelf Life (68°F/50% relative humidity) 2 years
Minimum Life Expectancy (based on accepted
application procedures on vertical surfaces) 8 years
Minimum Application Temperature 46°F
Available Lengths
Available Widths
150’ (50-yard), 30’ (10-yard)
24”, 30”, 54”
Recommended to be used in combination with ORAJET® Series 3850, 3676, 3675,
3551, 3551RA, 3551DT
UV Protection Extension Factor +4 years
For best results, utilize ORAFOL ICC profiles available at www.orafolamericas.com and allow solvent-based inks to dry for at least 24 hours
(48-72 hours preferred) at 70°F before cutting the graphic to the ink or applying a laminate.
Note
Surfaces to which the material will be applied must be thoroughly cleaned from dust, grease or any contamination which could affect the
adhesion of the material. Freshly lacquered or painted surfaces should be completely cured. The compatibility of selected lacquers and
paints should be tested by the user, prior to application of the material. Films with structured surface are naturally more sensitive than the
unstructured. Accordingly, these films are to be treated carefully both in processing and in cleaning. Impurities affect the appearance of
structured films and require more frequent cleaning. Furthermore the application information published by ORAFOL is to be considered. The
batch traceability according to ISO 9001 is possible on the basis of the roll number.