Arlon 5000 High Gloss Calendered Vinyl Film color #104 gold medal
Arlon 5000 High Gloss Calendered Vinyl FilmSeries 5000 is an ultra thin 2.8-mil (70 micron) calendered film and is one of the most pliable calendered films on the
market. The product has a high gloss finish, and is ideal for signs, graphics or displays requiring vibrant color. This film is
available in 37 bright colors and provides excellent cutting and weeding for improved productivity and has an outdoor
durability rating of up to 6 years.
Series 5000, an ultra thin 2.8-mil (70 micron) calendered film is one of the most pliable calendered films on the market. The product has a high gloss finish, and is ideal for signs, graphics or displays requiring vibrant color. This film is available in 37 bright colors, provides excellent cutting and weeding for improved productivity and has an outdoor durability rating of up to 6 years.
Applications & Features
- Available in 37 colors
- Easy to handle 2.8-mil (70 micron) calendered film
- Cutting and weeding performance speeds up your sign production*
- Recommended for flat and soft curved surfaces
- Gloss finish is excellent for banners, interior and exterior graphics
- Up to 6-years outdoor durability
Performance & Physical Data
| Property | Test Methods | Typical Value | |
|---|---|---|---|
| Surface Finish | Colors: Gloss Meter 60° Reflection | 75 to 85 Gloss Units | |
| Thickness | Micrometer, Federal Bench Type | 2.8-mil (70 micron) | |
| Tensile Strength | Tensile Tester with 2-in (51 mm) jaw separation; crosshead speed of 12 in/min. (5.1 mm/s), web direction | 12 lb/in width | 2.1 kg/cm width |
| Elongation | Instron Tensile Tester as above | ≥ 150% | |
| Shelf Life | Free from excessive moisture, temperature, direct sunlight | 1 year from factory shipment | |
| Application Temperature Range | On clean, dry substrate | 60°F to 90°F optimum | 15°C to 32°C optimum |
| Service Temperature Range | Film applied to etched aluminum panels 24 hours prior to testing | -40°F to 150°F | -40°C to 65°C |
| Humidity Resistance | Film applied to etched aluminum panels 24 hours prior to testing; 100% relative humidity at 100°F (38°C) for 24 hours | No appreciable effect | |
| Gasoline Resistance | Film applied to etched aluminum panels 24 hours prior to testing; immersed 15 minutes at 70°F (21°C); stabilized 24 hours before inspection | No appreciable effect | |
| Dimensional Stability | 158°F (70°C), 48 hours | 0.025 in | 0.64 mm nominal |
| Peel Adhesion | PSTC-1, 15 min, RT 72°F (23°C) | ≥ 40 oz/in | ≥ 0.45 kg/cm |
| Liner Release | TLMI 300 in/min (762 cm/min) | 150 g/2 in | 30 g/cm 0.75 n/25 mm |