Description
Arlon DPF 8200X High Tack
With the combination of a unique low-shrink, high tack adhesive system and bubble releasing X-Scape Technology®, DPF 8200X High Tack will adhere especially well to smooth surfaces along with slightly textured wall substrates such as brick, tile, and concrete. Graphic application is now easier and more efficient minimizing the potential for bubbles during installation. With reduced converting and printing time, you can remain focused producing brilliant graphics. DPF 8200X High Tack is compatible with a wide variety of print systems including Eco-Solvent, Solvent, Latex, and UV.
Unique Features
- Low Profile X-Scape Technology® for Easy, Bubble-Free Installations
- Easy to Convert, Print, and Apply, Optimizing your Workflow
- Low Shrink Adhesive System
- Strong Adhesion for Demanding Applications
| Property | Test Methods | Typical Value | |
|---|---|---|---|
| Surface Finish | Gloss Meter 60° Reflection | 40 to 60 Gloss Units | |
| Thickness | Micrometer, Federal Bench Type | 3.5-mil (90 micron) | |
| Tensile Strength | Tensile Tester with 2-in (51 mm) jaw separation; crosshead speed of 12 in/min. (5.1 mm/s), web direction | 13.0 lb/in | 2.3 kg/cm |
| Elongation | Instron Tensile Tester as above | > 150% | |
| Shelf Life (In Box) | Ideal Storage Temperature 70°F (21°C) and 50% relative humidity | 1 year from factory shipment | |
| Application Temperature Range | On clean, dry substrate | 50°F to 80°F optimum | 10°C to 27°C optimum |
| Service Temperature Range | On clean, dry substrate | -65°F to 225°F | -54°C to 107°C |
| Dimensional Stability | 158°F (70°C), 48 hours | < 50 mil | < 1.27 mm |
| Peel Adhesion | PSTC-1, 15 min, 70°F (21°C) | 4.0 lb/in | 0.71 kg/cm |
| Liner Release | TLMI Release at 90˚, 300 in/min (760 cm/min) | 50 g/2 in | 9.8 g/cm |