Avery Dennison DOL 1460Z High Gloss Clear Conformable Cast Overlaminate

Description

Avery Dennison DOL 1460Z High Gloss Clear Conformable Cast Overlaminate

Avery Dennison® DOL 1460Z High Gloss
High Gloss Clear Conformable Cast Overlaminate
Features
• Conformable film with excellent deep recess (channel) and compound
curve performance in combination with our MPI 1105 series ultimate
cast films
• Provides maximum UV and weathering protection with added abrasion
and chemical resistance to printed graphics. Improves solvent, UV
curable and latex inkjet outdoor image durability up to 5 years
• Wet paint-like look high gloss finish
• Brilliant transparency for bright, vivid images
• Dimensionally stable mottle reduction PET liner for easy converting
• Exceptional adhesion to solvent inkjet, UV curable inkjet, latex inkjet
and screen printed graphics
• Excellent adhesive contact to UV curable inks with no “silvering”
• Provides extra “body” to finished graphics for improved application
performance without the need for application tape
Description
Film: 30 micron high gloss
clear conformable UV stable
cast vinyl overlaminate
Adhesive: Permanent acrylic
Backing: One side coated
transparent PET film, 50
micron
Outdoor life: Up to 7 years
Conversion
Flat bed cutters Cold overlaminating
Friction fed cutters Latex inkjet
Die cutting Eco-solvent inkjet
Thermal transfer Solvent inkjet
Screen printing UV Cured inkjet
Common Applications
•
•
•
•
Flat sided trucks
Corrugated trucks
Cars and vans
Marine
Application
• For processing tips and reference guides please refer to Avery Dennison Instructional Bulletins:
• 4.06 Processing Tips for Avery Dennison DOL Films
Uses
Avery Dennison DOL1460Z High Gloss is a conformable premium quality UV
stable high gloss cast overlaminate designed for use as a protective
overlaminating film for digitally printed images and is suitable for durable
outdoor images on irregular surfaces, such as vehicles, where high gloss
finish and the excellent conformability is necessary.
Avery Dennison Graphics Solutions Asia Pacific
www.graphicsap.averydennison.com
General
Calliper, face film ISO 534 30 micron
Calliper, face film & adhesive ISO 534 55 micron
Dimensional stability DIN 38464 0.4mm Max
Tensile Strength DIN 53455 0.5-1.25 kg/cm
Elongation DIN 53455 > 150%
Gloss ISO 2813, 60o 90%
Adhesion, initial ASTM 1000, stainless steel 525 N/m
Adhesion, ultimate ASTM 1000, stainless steel 613 N/m
Flammability Self extinguishing
Shelf life Stored at 22° C/50-55 % RH 2 years
Expected Durability ** Vertical exposure Up to 7 years
Thermal
Min. Application Temperature + 4 o
C
Lamination temperature See relevant technical bulletins
Service temperature range – 40o
C to + 80o
C
Chemical
Resistant to most mild acids, alkalis and salts
Important
Information on physical characteristics is based
upon tests we believe to be reliable. The values
listed herein are typical values and are not for use
in specifications.
They are intended only as a source of information
and are given without guarantee and do not
constitute a warranty. Purchasers should
independently determine, prior to use, the
suitability of any material for their specific use.
All technical data is subject to change without
prior notice.
Warranty
Avery Dennison® materials are manufactured
under careful quality control and are warranted to
be free from defect in material and workmanship.
Any material shown to our satisfaction to be
defective at the time of sale will be replaced
without charge. Our aggregate liability to the
purchaser shall in no circumstances exceed the
cost of the defective materials supplied. No
salesman, representative or agent is authorised
to give guarantee, warranty, or make any
representation contrary to the foregoing.
All Avery Dennison® materials are sold subject to
the above conditions, being part of our
standard conditions of sale, a copy of which is
available on request.
**Expected Durability
The expected durability of Avery Dennison films
are defined as the expected performance life of
the Avery Dennison graphic film(s) within Zone 1
of the Avery Dennison zone system, in outdoor
vertical exposure conditions.
The actual performance life will depend on a
variety of factors, including selection and
preparation of substrate, angle and direction of
exposure, application methods, environmental
conditions and cleaning/maintenance of the films.
In case of films used in areas of high
temperatures or humidity, high altitudes and
industrially polluted areas the performance will be
further reduced.
Expected Durability and Warranted Period
Definitions
Expected durability is the expected period of
time defined in the product data sheet, the
product should, but is not warranted to, perform
satisfactorily when applied in vertical exposure
conditions as defined in Instructional Bulletin
1.30. The warranted period as defined in the
appropriate ICS Performance Guarantee Bulletin,
is the maximum period of time Avery Dennison
will warrant the finished products performance in
accordance with ICS Performance Guarantee
Terms and Conditions 1.0, provided that the film
is properly stored, converted and installed in
accordance with Avery Dennison guidelines.
Dimensional stability:
Is measured on a 150 x 150 mm aluminium panel to which
a specimen has been applied; 72 hours after application
the panel is exposed for 48 hours to + 70°C, after which
the shrinkage is measured.
Adhesion:
(FTM-1, FINAT) is measured by peeling a specimen at a
180° angle from a stainless steel or float glass panel, 24
hours after the specimen has been applied under
standardised conditions. Initial adhesion is measured 20
minutes after application of the specimen.
Flammability:
A specimen applied to aluminium is subjected to the flame
of a gas burner for 15 seconds. The film should stop
burning within 15 seconds after removal from the flame.
Temperature range:
A specimen applied to stainless steel is exposed at high
and low temperatures and brought back to room
temperature. 1 hour after exposure the specimen is
examined for any deterioration. Note: Prolonged exposure
to high and low temperatures in the presence of chemicals
such as solvents, acids, dyes, etc. may eventually cause
deterioration.
Chemical Resistance:
All chemical tests are conducted with test panels to which
a specimen has been applied. 72 hours after application
the panels are immersed in the test fluid for the given test
period. 1 hour after removing the panel from the fluid, the
specimen is examined for any deterioration.
Corrosion Resistance:
A specimen applied to aluminium is exposed to saline mist
(5% salt) at 35ºC. After exposure, the film is removed and
the panel is examined for traces of corrosion.
Test Methods
Avery Dennison® DOL 1460Z High Gloss Rev. 0 (Aug 2016)

A116020 DOL1460Z GLOSS PERM PET
A116018 DOL1460Z GLOSS PERM PET
A006170 DOL1460Z GLOSS PERM PET
A005562 DOL1460Z GLOSS PERM PET
A006171 DOL1460Z GLOSS PERM PET
A006172 DOL1460Z GLOSS PERM PET
A005938 DOL1460Z GLOSS PERM PET
A006173 DOL1460Z GLOSS PERM PET
A010531 DOL1460Z GLOSS PERM PET