Avery MPI3729 PERFORATED FILM 60/40 7 mil White/Black vinyl with removable adhesive for one-way visual panels

Description

Avery MPI3729 PERFORATED FILM 60/40 7 mil White/Black vinyl with removable adhesive for one-way visual panels
Avery Dennison®
MPI 3729 Perforated
Window Film 60/40 is a perforated flexible
calendered film for use on exterior-mount oneway
visual panels. Graphics printed on this
material are visible from the front and
“invisible” from the back when mounted on
windows. MPI 3729’s 60/40 perforation
pattern provides a print area of 60% allowing
for better image quality on a one-way graphic
panel. This film is intended for stationary
windows or for applications where visibility of
the printed graphic is more important than
visibility through the film.

BCI Imaging Supplies

Avery Dennison® MPI 3729
Perforated 60/40
PE Coated non-perforated kraft
Revision: 0 Dated: 06/12/14
Product Data Sheet
Page 1 of 3
averygraphics.com
AnswerLine: 800-231-4654
Uses:
Avery Dennison®
MPI 3729 Perforated
Window Film 60/40 is a perforated flexible
calendered film for use on exterior-mount oneway
visual panels. Graphics printed on this
material are visible from the front and
“invisible” from the back when mounted on
windows. MPI 3729’s 60/40 perforation
pattern provides a print area of 60% allowing
for better image quality on a one-way graphic
panel. This film is intended for stationary
windows or for applications where visibility of
the printed graphic is more important than
visibility through the film.
Face: 6 mil (150 microns)
white/black perforated calendered
vinyl
Adhesive: Removable Acrylic
Liner: One side PE coated nonperforated
kraft paper, (168 g/m2
)
Durability: Up to 1 year (unprinted)
Application
Surfaces:
Flat, simple curves
Features:
• Perforated film with white print face, black on adhesive side for one-way vision graphics.
• 1.5 mil hole provides light transmission with 40% open area
• 60/40 hole pattern allows a 60% printable surface area to achieve a higher image quality
for stationary graphics.
• Good outdoor durability
• Good dimensional stability
• Good adhesion level on glass substrates
• Good image clarity and color pop
• Provides a reduction of indoor solar heat gain for window applications
Conversion:
• Screen Printing
• Solvent based inkjet
• Mild/Eco Solvent inkjet
• UV inkjet
• Latex
Common Applications:
• Window Graphics
• Building Wraps
• Retail Signage
• Commercial Signage
• Bus Shelters
• POP Displays
• Other Transparent Surfaces

Avery Dennison® MPI 3729
Perforated 60/40
PE Coated non-perforated kraft
Revision: 0 Dated: 06/12/14
Product Data Sheet
Page 2 of 3
averygraphics.com
AnswerLine: 800-231-4654
Physical Characteristics:
Property Value
Caliper, face 6 mil (150µm)
Caliper, adhesive 1.0 mil (25 µm)
Open Area 40% (approx)
Perforation Diameter 1.5 mm
Dimensional stability <0.02” (0.5mm)
Note: Ink loads in excess of 250% may cause
increased shrinkage of the printed film.
Tensile at Yield N/A
Elongation N/A
Gloss N/A
Adhesion:
24 hr Stainless
Glass
0.86 lbs/in (144 N/m)
0.9 lbs/in (158 N/m)
Removability Smooth OEM
Painted Surfaces
1 year
NOTE: Not when applied to:
Nitrocellulose paint, ABS, Polystyrene,
screen printing inks (fresh), certain types of
PVC, Polycarbonate or PMMA
Flammability Self Extinguishing
Shelf-Life Stored at 70°F
(22°C) / 50-55%
RH
1 year
Durability Vertical Exposure Up to 1 year unprinted
Min. Application
Temperature
50° F (10° C)
Service Temperature -4°-149°F (-20°-65° C) (Reasonable
range of temperatures which would
be expected under normal
environmental conditions).
Chemical resistance Resistant to most mild acids, alkalis,
and salt solutions.
If not overlaminated, the unprinted
perforated window film is resistant to
water, humidity, solvents, most acids,
alkalis and salt. Due to the open
structure of the film, exposure should
be limited to an absolute minimum.
Overlaminated perforated window film
has the same resistance to chemical
substances as the overlaminated film.
NOTE: Materials have to be properly dried and cured before further processing like laminating,
varnishing, trimming, contour cutting or application. The residual solvents can otherwise change
the products’ specific features and properties.
Important:
Information on physical and chemical characteristics
are based on tests believed to be reliable. The values
are intended only as a source of information. This
information is given without guaranty and do not
constitute a warranty. The purchaser should
independently determine, prior to use, the suitability of
any material for their specific purpose. (Data
represents average values where applicable, and is
not intended for specification purposes)
Warranty:
All statements, technical information and
recommendations about Avery Dennison
products are based upon tests believed to be
reliable but do not constitute a guarantee or
warranty. All Avery Dennison products are sold
with the understanding that Purchaser has
independently determined the suitability of such
products for its purposes. Avery Dennison
products are warranted to be free from defects in
material and workmanship for either one year (or
the period stated on the specific product
information literature in effect at time of delivery, if
longer) from date of shipment if said product is
properly stored and applied. It is expressly agreed
and understood that Avery Dennison’s sole
obligation and Purchaser’s exclusive remedy
under this warranty, under any other warranty,
express or implied, or otherwise, shall be limited
to repair or replacement of defective product
without charge at Avery Dennison’s plant or at the
location of product (at Avery Dennison’s election),
or in the event replacement or repairs is not
commercially practical, to Avery Dennison’s
issuing Purchaser a credit reasonable in light of
the defect in the product.
Avery Dennison’s liability for defective products
shall not exceed the purchase price paid
therefore by Purchaser and in no event shall
Avery Dennison be responsible for any incidental
or consequential damages whether foreseeable
or not, caused by defects in such product,
whether such damage occurs or is discovered
before or after replacement or credit, and whether
or not such damage is caused by Avery
Dennison’s negligence.
NO EXPRESS WARRANTIES AND NO IMPLIED
WARRANTIES, WHETHER OF
MERCHANTABILITY OR FITNESS FOR ANY
PARTICULAR USE, OR OTHERWISE (EXCEPT
AS TO TITLE), OTHER THAN THOSE
EXPRESSLY SET FORTH ABOVE WHICH ARE
MADE EXPRESSLY IN LIEU OF ALL OTHER
WARRANTIES, SHALL APPLY TO PRODUCTS
SOLD BY AVERY DENNISON. AVERY
DENNISON SPECIFICALLY DISCLAIMS AND
EXCLUDES ALL OTHER SUCH WARRANTIES.
NO WAIVER, ALTERATION, ADDITION OR
MODIFICATION OF THE FOREGOING
CONDITIONS SHALL BE VALID UNLESS MADE
IN WRITING AND MANUALLY SIGNED BY AN
OFFICER OF AVERY DENNISON.

Avery Dennison® MPI 3729
Perforated 60/40
PE Coated non-perforated kraft
Revision: 0 Dated: 06/12/14
Product Data Sheet
Page 3 of 3
averygraphics.com
AnswerLine: 800-231-4654
Dimensional stability:
Is measured on a 6” x 6” (150 x 150 mm)aluminum panel to which a specimen has been applied; 72 hours after
application the panel is scored in a cross pattern, exposed for 48 hours to 150°F (65°C), after which the shrinkage is
measured.
Removability:
“Removable Adhesive” means an Avery Dennison® adhesive that can be removed without heat or chemicals within the
period stated on the respective Product Data Sheet and might leave twenty percent (20%) or less adhesive residue.
This product is not removable when applied to: Nitrocellulose paint, ABS, Polystyrene, screen printing inks (fresh), certain
types of PVC, Polycarbonate or PMMA
Adhesion:
(FTM-1, FINAT) is measured by peeling a specimen at a 180° angle from a stainless steel panel, 24 hours after the
specimen has been applied under standardized conditions. Initial adhesion is measured 15 minutes after application of
the specimen.
Flammability:
A specimen applied to aluminum is subjected to the flame of a gas burner for 15 seconds. The film should stop burning
within 15 seconds after removal from the flame.
Temperature range:
A specimen applied to stainless steel is exposed at high and low temperatures and brought back to room temperature.
One hour after exposure the specimen is examined for any deterioration. Note: Prolonged exposure to high and low
temperatures in the presence of chemicals such as solvents, acids, dyes, etc. may eventually cause deterioration.
Chemical Resistance:
All chemical tests are conducted with test panels to which a specimen has been applied 72 hours after application the
panels are immersed in the test fluid for the given test period. One hour after removing the panel from the fluid, the
specimen is examined for any deterioration.
Special Considerations:
Because of the unique properties and varieties of glass, special considerations must be considered for windows and
graphic applications. Avery Dennison® accepts no liability for glass breakage.
• Glass absorbs heat when exposed to sunlight. The degree of absorption across windows can vary because of
shading, heating, and cooling ventilation, and insulation from window frames. These temperature differences across
the window produce stress, which can cause glass breakage. The ability of glass to resist breakage because of
temperature stress is affected by window size, glass thickness, glass treatments, quality, and design.
• Window cleaning methods also vary, from the type of cleaners used, to the washing methods employed. Specific
chemicals used in window cleaners may affect the adhesion of pressure-sensitive graphics. Power washing
methods may impact the adhesion of graphics if the water pressure or temperature exceeds the graphic’s adhesion
capability.
Revisions are italicized
Avery Dennison is a registered trademark of Avery Dennison Corp.
Avery MPI3729 PERFORATED FILM 60/40 7 mil White/Black vinyl with removable adhesive for one-way visual panels 6206 6207 5980 5979