Description

Océ WC6VY – WALL COVERING VINYL W/ PSA

Description
6-mil, economical, soft PVC film featuring a special low-tack adhesive that enables the graphic to be removed easily.
Available in white with a matte surface.
Release Liner
83# silicone-coated paper
Adhesive
Clear, water-based, removable adhesive
Area of Use
Designed for shorter-term interior contour-cut wall and window graphics. (An unprinted border around the graphic is
recommended to help ensure the success of the application)
Technical Data
Thickness (without liner and adhesive) 6-mil
Dimensional Stability (FINAT TM-14) Adhered to steel, no shrinkage in cross direction;
In length, <.016”
Temperature Resistance Adhered to aluminum, -40°F to +176°F, no variation
Fire Behavior (DIN 75200)
Fire Rating
Adhered to steel, self-extinguishing
ASTM E 84-07 Class “A”
Adhesive Power (FINAT TM-1, after 24 h, average) Adhered to stainless steel: 1.36 lb/in
Tensile Strength (DIN EN ISO 527) Along: Min. 30 MPa
Across: Min. 28 MPa
Elongation at Break (DIN EN ISO 527) Along: Min. 180%
Across: Min. 200%
Seawaterability (DIN 50 021) Adhered to aluminum, after 100h/73°F, no variation
Shelf Life (68°F/50% relative humidity) 2 years
Minimum Life Expectancy (based on accepted
application procedures on vertical surfaces) 2 years (unprinted; original application only)
Minimum Application Temperature 50°F
Available Lengths
Available Widths
150’ (50-yard)
30”, 54”, 60”

Print Compatibility Latex, Solvent, Eco-Solvent, UV Curable
For best results, utilize ORAFOL ICC profiles available at www.orafolamericas.com and allow solvent-based inks to dry for at least 24 hours
(48-72 hours preferred) at 70°F before cutting the graphic to the ink or applying a laminate.
Note
Surfaces to which the material will be applied must be thoroughly cleaned from dust, grease or any contamination which could affect the
adhesion of the material. Freshly lacquered or painted surfaces should be completely cured. The compatibility of selected lacquers and
paints should be tested by the user, prior to application of the material. Films with structured surface are naturally more sensitive than the
unstructured. Accordingly, these films are to be treated carefully both in processing and in cleaning. Impurities affect the appearance of
structured films and require more frequent cleaning. Furthermore the application information published by
batch traceability according to ISO 9001 is possible on the basis of the roll number.