Description
Oracal 7510 High Performance Fluorescents
Oracal 7510 High Performance Fluorescents
• The longest lasting fluorescent vinyl available anywhere.
• Up to 2-year outdoor durability.
• 6 mil cast film.
• Permanent adhesive.
http://www.orafol.com/tl_files/content/downloads/technicaldatasheets/europe/en/oracal/oracal-7510-eu-en.pdf
Description
High performance cast fluorescent film with high visibility when illuminated by all daylight conditions.
Especially effective in twilight and bad sight conditions.
Release paper
Silicone coated paper on one side, 137 g/m².
Adhesive
Solvent polyacrylate, permanent
Area of use
For outdoor applications. Designed for warning signs, vehicle and bus advertising, name plates and
graphics of all types that requires special high- impact visibility. Very good suitable for die-cut plotter
systems.
Printing method
Recommended is screen printing.
Thickness* 150 micron
Dimensional stability adhered to steel, no measurable shrinkage in cross direction,
in length 0.3 mm max.
Temperature resistance adhered to aluminium, -40°C to +110°C, no variation
Seawater resistance adhered to aluminium, after 100h/23°C no variation
Adhesive power*
(FINAT TM 1, after 24h, stainless steel)
18 N/25 mm
Tensile strength (DIN EN ISO 527)
along min. 15 MPa
across min. 15 MPa
Elongation at break (DIN EN ISO 527)
along mind. 120%
across mind. 120%
Shelf life** 2 years
Application temperature min. + 8°C
Service life by specialist application
under vertical outdoor exposure (normal climate of Central Europe)
2 years (not printed)
Attention:
Surfaces to which the material will be applied must be thoroughly cleaned from dust, grease or any
contamination which could affect the adhesion of the material. Freshly lacquered or painted surfaces should
be allowed to dry for at least three weeks and to completely cure respectively. The compatibility of selected
lacquers and paints should be tested by the user, prior to application of the material. Furthermore the
application informations published by ORAFOL are to be considered.