ORAFOL ORAGUARD 255AS Skid-Resistant PVC Laminating Film

Description

ORAFOL ORAGUARD 255AS Skid-Resistant PVC Laminating Film
ORAGUARD® 255AS SKID-RESISTANT PVC LAMINATING FILM FOR HIGH LOAD EXPOSURE
Description
6.5-mil, matte transparent PVC film with a raised, skid-resistant textured surface
Release Liner
55# silicone-coated paper
Adhesive
Clear, solvent-based, permanent adhesive
Area of Use
A cold laminate for anti-skid protection of floor graphics exposed to very high loads. Meets the standards
of ASTM D 2047 and BAM StVo §35 d3, (Federal Office for Material Testing: Automobile Safety Act).
Technical Data
Thickness (without liner and adhesive) 6.5-mil
Temperature Resistance Adhered to aluminum, -40°F to +176°F, no variation
Fire Behavior (DIN 75200)
Fire Rating
Adhered to steel, self-extinguishing
ASTM E 84-07 Class “A”
Adhesive Power (FINAT TM-1, after 24 h, average) Adhered to stainless steel: 2.74 lb/in
Tensile Strength (DIN EN ISO 527) Along: Min. 22 MPa
Across: Min. 22 MPa
Elongation at Break (DIN EN ISO 527) Along: Min. 130%
Across: Min. 150%
Seawaterability (DIN EN ISO 527) Adhered to aluminum, after 100h/73°F, no variation
Shelf Life (68°F/50% relative humidity) 2 years
Minimum Life Expectancy (based on accepted
application procedures on vertical surfaces) 6 months
Minimum Application Temperature 46°F
Available Lengths
Available Widths
150’ (50-yard)
36”, 40”, 50”, 54”
Recommended to be used in combination with ORAJET®
1663
System Skid Resistance (Federal Office for Material
Testing: Automobile Safety Act)
Skid Distance Dry: <35”
Skid Distance Wet: <55”
For best results, utilize ORAFOL ICC profiles available at www.orafolamericas.com and allow solvent-based inks to dry for at least 24 hours
(48-72 hours preferred) at 70°F before cutting the graphic to the ink or applying a laminate.