ORAFOL ORAJET 3164 Soft Calendered PVC Matte VINYL

Description

ORAFOL ORAJET 3164 Soft Calendered PVC Matte VINYL
Description
4-mil, soft calendered PVC film in white with a gloss or matte surface and in transparent with a gloss surface.
UL certified for UL 969 “Marking and Labeling Systems” (USA) and CSA C22.2 No. 0.15 “Adhesive Labels” (Canada).
Release Liner
83# PE coated silicone paper
Adhesive
Clear, water-based, permanent adhesive
Area of Use
For economical general signage, short- to medium-term flat indoor and outdoor applications including decals, nameplates,
die cut letters and POP displays.
Technical Data
Thickness (without liner and adhesive) 4-mil
Dimensional Stability (FINAT TM-14) Adhered to steel, no shrinkage in cross direction;
In length, <.016” Temperature Resistance Adhered to aluminum, -40°F to +176°F, no variation Fire Behavior (DIN 75200) Fire Rating Adhered to steel, self-extinguishing ASTM E 84-07 Class “A” Adhesive Power (FINAT TM-1, after 24 h, average) Adhered to stainless steel: 3.7 lb/in Tensile Strength (DIN EN ISO 527) Along: Min. 19 MPa Across: Min. 19 MPa Elongation at Break (DIN EN ISO 527) Along: Min. 130% Across: Min. 150% Seawaterability (DIN 50 021) Adhered to aluminum, after 100h/73°F, no variation Shelf Life (68°F/50% relative humidity) 2 years Minimum Life Expectancy (based on accepted application procedures on vertical surfaces) 4 years (unprinted) Minimum Application Temperature 50°F Available Lengths Available Widths White 150’ (50-yard) 30”, 50”, 54”, 60”, 80” Transparent 150’ (50-yard) 54” Recommended Laminates ORAGUARD® Series 200, 210 Print Compatibility Latex, Solvent, Eco-Solvent, UV Curable For best results, utilize ORAFOL ICC profiles available at www.orafolamericas.com and allow solvent-based inks to dry for at least 24 hours (48-72 hours preferred) at 70°F before cutting the graphic to the ink or applying a laminate. Note Surfaces to which the material will be applied must be thoroughly cleaned from dust, grease or any contamination which could affect the adhesion of the material. Freshly lacquered or painted surfaces should be completely cured. The compatibility of selected lacquers and paints should be tested by the user, prior to application of the material. Films with structured surface are naturally more sensitive than the unstructured. Accordingly, these films are to be treated carefully both in processing and in cleaning. Impurities affect the appearance of structured films and require more frequent cleaning. Furthermore the application information published by ORAFOL is to be considered. The batch traceability according to ISO 9001 is possible on the basis of the roll number.