ORAFOL ORAJET 3164 Soft Calendered PVC Transparent Gloss VINYL

Description

ORAFOL ORAJET 3164 Soft Calendered PVC transparent gloss VINYL
Description
4-mil, soft calendered PVC film in white with a gloss or matte surface and in transparent with a gloss surface.
UL certified for UL 969 “Marking and Labeling Systems” (USA) and CSA C22.2 No. 0.15 “Adhesive Labels” (Canada).
Release Liner
83# PE coated silicone paper
Adhesive
Clear, water-based, permanent adhesive
Area of Use
For economical general signage, short- to medium-term flat indoor and outdoor applications including decals, nameplates,
die cut letters and POP displays.
Technical Data
Thickness (without liner and adhesive) 4-mil
Dimensional Stability (FINAT TM-14) Adhered to steel, no shrinkage in cross direction;
In length, <.016”
Temperature Resistance Adhered to aluminum, -40°F to +176°F, no variation
Fire Behavior (DIN 75200)
Fire Rating
Adhered to steel, self-extinguishing
ASTM E 84-07 Class “A”
Adhesive Power (FINAT TM-1, after 24 h, average) Adhered to stainless steel: 3.7 lb/in
Tensile Strength (DIN EN ISO 527) Along: Min. 19 MPa
Across: Min. 19 MPa
Elongation at Break (DIN EN ISO 527) Along: Min. 130%
Across: Min. 150%
Seawaterability (DIN 50 021) Adhered to aluminum, after 100h/73°F, no variation
Shelf Life (68°F/50% relative humidity) 2 years
Minimum Life Expectancy (based on accepted
application procedures on vertical surfaces) 4 years (unprinted)
Minimum Application Temperature 50°F
Available Lengths
Available Widths
White
150’ (50-yard)
30”, 50”, 54”, 60”, 80”
Transparent
150’ (50-yard)
54”
Recommended Laminates ORAGUARD®
Series 200, 210
Print Compatibility Latex, Solvent, Eco-Solvent, UV Curable
For best results, utilize ORAFOL ICC profiles available at www.orafolamericas.com and allow solvent-based inks to dry for at least 24 hours
(48-72 hours preferred) at 70°F before cutting the graphic to the ink or applying a laminate.
Note
Surfaces to which the material will be applied must be thoroughly cleaned from dust, grease or any contamination which could affect the
adhesion of the material. Freshly lacquered or painted surfaces should be completely cured. The compatibility of selected lacquers and
paints should be tested by the user, prior to application of the material. Films with structured surface are naturally more sensitive than the
unstructured. Accordingly, these films are to be treated carefully both in processing and in cleaning. Impurities affect the appearance of
structured films and require more frequent cleaning. Furthermore the application information published by ORAFOL is to be considered. The
batch traceability according to ISO 9001 is possible on the basis of the roll number.